Assessment of the Microstructure and Solidification Characteristics of Al–۲۰%Mg۲Si Composite under Melt Superheating Treatment Using Thermal Analysis
Publish Year: 1400
نوع سند: مقاله ژورنالی
زبان: English
View: 122
This Paper With 9 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMSEI-18-3_008
تاریخ نمایه سازی: 24 بهمن 1401
Abstract:
The influence of melt superheating treatment on the solidification characteristics and microstructure of Al–۲۰%Mg۲Si in-situ composite has been investigated. The results revealed that melt superheating temperature has a significant effect on solidification parameters and morphology of primary Mg۲Si particles. Solidification parameters acquired using cooling curve thermal analysis method, indicate that both nucleation temperature and nucleation undercooling of primary Mg۲Si particles increase by increasing melt superheating temperature, while recalescence undercooling decrease under the same condition. Also, based on the microstructural evaluations, melt superheating treatment can refine primary Mg۲Si particles and alter their morphology from dendritic shape to more spherical shape and the eutectic microstructure of a-Al + Mg۲Si becomes finer and the distance between eutectic layers becomes smaller.
Keywords:
Al–۲۰%Mg۲Si in-situ composite , melt superheating treatment , cooling curve thermal analysis , microstructure , solidification
Authors
Saeed G. Shabestari
Professor of Materials EngineeringIran University of Science and Technology (IUST)
Sahar Ashkvary
School of Metallurgy and Materials Engineering, Iran University of Science and Technology (IUST), Narmak, Tehran, Iran
Farnaz Yavari
School of Metallurgy and Materials Engineering, Iran University of Science and Technology (IUST), Narmak, Tehran, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :