Resistance of Alkali-activated Slag Cement Against Sodium Sulfate
Publish Year: 1398
نوع سند: مقاله ژورنالی
زبان: English
View: 112
This Paper With 12 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMSEI-17-1_003
تاریخ نمایه سازی: 1 اسفند 1401
Abstract:
This work evaluates the resistance of alkali-activated slag (AAS) mortar against sodium sulfate attack. The effects of immersion in ۵% sodium sulfate solution under room temperature and wetting-drying cycles on the compressive strength of mortar specimens were considered for evaluating the extent of degradation. Mortar specimens prepared from type II and V Portland cements (PC۲ and PC۵) in accordance with ASTM standard were also used as reference. To characterize the chemical products of the degradation process due to sodium sulfate attack, the specimens were also studied by X-ray diffractometry, scanning electron microscopy, and the elemental analysis by energy dispersive X-ray spectroscopy. After ۳۶۰ days of exposure to the sodium sulfate solution, PC۲, PC۵ and AAS cements showed ۷۱, ۵۲ and ۴۵% reduction in compressive strength, respectively. According to the obtained results, AAS cement exhibits a higher sulfate resistance compared to PC۲ and PC۵.
Keywords:
Authors
A. Allahverdi
Iran University of Science and Technology
H. Hashemi
Iran University of Science and Technology
M. Mahinroosta
Iran University of Science and Technology
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :