Effect OF SI and AL on the Microstructure, Mechanical Properties and Machinability of ۶۵CU-۳۵ZN Brass
Publish Year: 1398
نوع سند: مقاله ژورنالی
زبان: English
View: 95
This Paper With 12 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMSEI-16-2_003
تاریخ نمایه سازی: 1 اسفند 1401
Abstract:
Relations between the microstructure, mechanical properties and machinability of as-cast ۶۵Cu-۳۵Zn brass with various amounts of Al from ۰ to ۴.۷۲ and Si from ۰ to ۳.۶۲ wt% were investigated. Both Si and Al initially enhanced the UTS and toughness of the brass samples, which led to improvement in machinability due to a reduction in the main cutting force. A duplex brass with random oriented α plates in β’ matrix was found to have the best machinability among the other microstructures. It was found that beside the presence of brittle phases, such as β’ phase in the microstructure, the morphology and hardness of the phases involved had significant influence on machinability.
Keywords:
Authors
M. Adineh
Shahid Bahonar University of Kerman
H. Doostmohammadi
Shahid Bahonar University of Kerman
R. Raiszadeh
Shahid Bahonar University of Kerman
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :