The Effects of ZnO Additive on Sintering Behavior, Microstructural Evolution and Microwave Dielectric Properties of Li۲TiO۳ Ceramics
Publish Year: 1397
نوع سند: مقاله ژورنالی
زبان: English
View: 133
This Paper With 10 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMSEI-16-1_001
تاریخ نمایه سازی: 1 اسفند 1401
Abstract:
The densification behavior, structural and microstructural evolution and microwave dielectric properties of Li۲TiO۳ + xZnO (x = ۰, ۰.۵, ۱, ۱.۵, ۲, ۳, and ۵ mol%) ceramics have been investigated using X-ray diffraction, Field Emission Scanning Electron Microscopy, Raman spectroscopy and microwave resonant measurement. The Maximum density of ۳.۳۳ g/cm۳ was obtained in Li۲TiO۳ + ۲ZnO ceramic at low sintering temperature of ۱۱۰۰˚C. SEM investigations revealed good close packing of grains when x = ۲ and preferential grain growth when x ≥ ۳. The maximum values of Q × f = ۳۱۸۰۰ GHz and εr = ۲۲.۵ were obtained in Li۲TiO۳ + ۳ZnO and Li۲TiO۳ + ۲ZnO compositions, respectively. The observed properties are attributed to the microstructural evolution and grain growth (first case) or high density of the obtained ceramic (second case).
Keywords:
Authors
T. Ebadzadeh
Materials and Energy Research Center
S. Ghaffari
Materials and Energy Research Center
M. Alizadeh
Materials and Energy Research Center
K. Asadian
Materials and Energy Research Center
Y. Ganjkhanlou
University of Pardubice
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :