Green synthesis and characterization of NiFe۲O۴ nanostructure via hydrothermal method
Publish place: Colloid and Nanoscience Journal، Vol: 1، Issue: 1
Publish Year: 1402
نوع سند: مقاله ژورنالی
زبان: English
View: 120
This Paper With 6 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_CNJ-1-1_001
تاریخ نمایه سازی: 26 فروردین 1402
Abstract:
In this paper nickel ferrite nanostructures fabricated via simple and green hydrothermal method using lemon juice. For the synthesis of NiFe۲O۴ nanoparticles, the materials were placed in the autoclave reactor for ۲ and ۱۲ hours. The morphology of particles was studied by scanning electron microscope (SEM). Although the NiFe۲O۴ nanoparticles after ۲ h heating are agglomerated but increasing the heating time to ۱۲ h leads to formation of sphere shape nano size particles. Crystal structure of nickel ferrite nanoparticles was investigated via X-ray diffraction pattern and crystallite size of particles was calculated using Debye-Scherrer formula. The magnetic hysteresis loop of the synthesized ferrite was studied by a vibration sample magnetometer (VSM). The magnetic parameters of remanance Mr, saturation magnetization Ms and coercivity Hc, increase as the synthesis time increases. The optical properties of NiFe۲O۴ were investigated by ultraviolet visible (UV-vis) spectra. The results show that the particles band gaps decreases with increasing the synthesis time.
Keywords:
Authors
Tavus Hosseinabad
Department of Physics,Faculty of Science, Arak University, Arak, Iran
Gholamreza Nabiyouni
Department of Physics,Faculty of Science, Arak University, Arak, Iran
Kambiz Hedayati
Department of Science, Arak University of Technology, Arak, Iran