Experimental Investigation of Brick-Slabs: Evaluation of the Performance and Ductility of Various Brick Materials
Publish Year: 1402
نوع سند: مقاله ژورنالی
زبان: English
View: 98
This Paper With 9 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJE-36-9_007
تاریخ نمایه سازی: 13 مرداد 1402
Abstract:
In this study, five one-way brick slab specimens were manufactured to investigate the behavior of brick slabs composed of various types of bricks (solid bricks, perforated bricks, and cellular concrete blocks (thermostone). The span ranges from ۶۰۰ to ۸۰۰ mm, while the camber ranges from ۰ to ۳۰ mm. Previously, cellular concrete blocks, solid and perforated clay bricks were employed as the building materials. These samples were tested by being subjected to flexural three-point loading. The results revealed that increasing camber by ۳۰ mm for solid brick specimens increased ductility, and ultimate strength, by ۵.۵% and ۷۷.۶۲, respectively. Increasing the span from ۶۰۰ to ۸۰۰ mm for solid brick specimens decreased the ultimate strength and ductility by ۳۷.۹۶% and ۶.۸۳%, respectively. Cellular concrete blocks can be used in the construction of slabs due to their lightweight and acceptable structural response when compared to solid brick specimens. Due to their good structural performance and lightweight, perforated bricks can be used to build brick slabs. Brittleness and the sudden collapse of the brickwork arch characterized the failure mode in all samples.
Keywords:
Authors
A. Hatif Obaid
Department of Civil Engineering, University of Misan, Amarah, Maysan ۶۲۰۰۱, Iraq
A. A. Jaafar
Department of Civil Engineering, University of Misan, Amarah, Maysan ۶۲۰۰۱, Iraq
E. Noroozinejad Farsangi
Faculty of Civil and Surveying Engineering, Graduate University of Advanced Technology, Kerman, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :