EFFECT OF COOLING RATE AND GRAIN REFINEMENT ON THE MICROSEGREGATION IN Al-۴.۸ wt.% Cu ALLOY
Publish Year: 1394
نوع سند: مقاله ژورنالی
زبان: English
View: 81
This Paper With 9 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMSEI-12-4_008
تاریخ نمایه سازی: 26 مرداد 1402
Abstract:
Microsegregation is one of the most important phenomena occurs during solidification. It usually results in formation of some unexpected second phases which generally affect the mechanical properties and specially reduce the workability of casting products. The aim of this research is to study the effect of cooling rate and grain refinement on the microsegregation in Al-۴.۸ wt.% Cu. For this purpose two series of experiments were designed. In the first set of experiments, the alloy was melted and cooled in three different rates, i.e. ۰.۰۴, ۰.۴۲, and ۱.۰۸ K/s in a DTA furnace. In the second series of experiments, the effect of grain refinement on the microsegregation at a constant cooling rate of ۰.۱۹ K/s was investigated. Al-۵Ti-۱B master alloy was used as grain refiner. Results showed that by increasing the cooling rate the amount of non-equilibrium eutectic phase increases from ۵.۱ to ۷.۴ wt.%, and the minimum concentration of solute element in primary phase decreases from ۱.۵۱ to ۱.۰۵ wt.% Cu. By grain refinement of the alloy, the amount of non-equilibrium eutectic phase decreases from ۵.۵ to ۴.۷ wt.%, and the minimum concentration of solute element in the primary phase increases from ۰.۹۸ to ۱.۰۷ wt.% Cu. So it is concluded that increasing cooling rate in the range of ۰.۰۴ to ۱.۰۸ K/s, increases and grain refinement reduces the microsegregation
Keywords:
Authors
M. Dehnavi
۱- Department of Materials Engineering and Metallurgy, Ferdowsi University of Mashhad, Mashhad, Iran
M. Haddad-Sabzevar
۱- Department of Materials Engineering and Metallurgy, Ferdowsi University of Mashhad, Mashhad, Iran
M.H. Avazkonandeh-Gharavol
۱- Department of Materials Engineering and Metallurgy, Ferdowsi University of Mashhad, Mashhad, Iran
H. Vafaeenezhad
School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Tehran, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :