Investigation of Hardness and Impact Toughness of Zr-Microalloyed Cast Steel
Publish Year: 1384
نوع سند: مقاله ژورنالی
زبان: English
View: 145
This Paper With 5 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ISSIRAN-2-1_004
تاریخ نمایه سازی: 5 شهریور 1402
Abstract:
Microalloyed cast steels are a group of microalloyed steels in which reliable mechanical properties could be achieved by heat treatment. In this work, the heat treatment processes were carried out on the cast specimens as the step samples by different thicknesses and Zr content. The results show that after homogenization, variations in thickness have no effect on the hardness. Also, after heat treatment, Zr has more effects on properties. The optimum austenitization time was determined ۲ hours in ۹۵۰°C. Aging has no effect on hardness on Zr- microalloyed cast steels
Keywords:
Authors
H. Aliakbarzadeh
Maham Institute of Science & Technology, Group of Munitions & Metallurgical Industries, Pasdaran, Tehran, Iran
Sh. Mirdamadi
Department of Metallurgy and Engineering Materials, Iran University Science and Technology, Narmak, Tehran, Iran
M. Tamizifar
Department of Metallurgy and Engineering Materials, Iran University Science and Technology, Narmak, Tehran, Iran
M. Saleh
Maham Institute of Science & Technology, Group of Munitions & Metallurgical Industries, Pasdaran, Tehran, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :