Influences of mechanical activation and tartaric acid addition on the efficiency of B۴C synthesis

In this paper, mechanical activation and tartaric acid addition were employed to reduce the residual carbon and intensify the efficiency of B۴C synthesis using glucose and boric acid as starting materials. To investigate the role of mechanical activation on synthesis performance, one sample was subjected to high-energy ball milling before pyrolysis and the other after pyrolysis. To study the role of additives, in the precursor production stage, on synthesis efficiency and residual carbon reduction, different amounts of tartaric acid (۰, ۵, ۱۰, ۲۵, and ۵۰ wt%) were tested. FT-IR and XRD analyses were used to characterize the bonds created in the precursors and the phases formed during the pyrolysis and synthesis steps, respectively. The results confirmed that mechanical activation before synthesis can improve the synthesis efficiency, but ball milling before pyrolysis did not significantly affect the final synthesis product. The addition of tartaric acid enhanced the formation of B–C bonds; hence, it increased the efficiency of B۴C synthesis. The optimum additive amount was ۲۵ wt% and higher amounts weakened the synthesis performance.In this paper, mechanical activation and tartaric acid addition were employed to reduce the residual carbon and intensify the efficiency of B۴C synthesis using glucose and boric acid as starting materials. To investigate the role of mechanical activation on synthesis performance, one sample was subjected to high-energy ball milling before pyrolysis and the other after pyrolysis. To study the role of additives, in the precursor production stage, on synthesis efficiency and residual carbon reduction, different amounts of tartaric acid (۰, ۵, ۱۰, ۲۵, and ۵۰ wt%) were tested. FT-IR and XRD analyses were used to characterize the bonds created in the precursors and the phases formed during the pyrolysis and synthesis steps, respectively. The results confirmed that mechanical activation before synthesis can improve the synthesis efficiency, but ball milling before pyrolysis did not significantly affect the final synthesis product. The addition of tartaric acid enhanced the formation of B–C bonds; hence, it increased the efficiency of B۴C synthesis. The optimum additive amount was ۲۵ wt% and higher amounts weakened the synthesis performance.

Keywords:

B۴C , Synthesis efficiency , Mechanical activation , Tartaric acid addition , Residual carbon