Effective Use of Sacrificial Zinc Anode as a Suitable Repair Method for Severely Damaged RC Members Due to Chloride Attack
Publish place: Civil Engineering Journal، Vol: 8، Issue: 7
Publish Year: 1401
نوع سند: مقاله ژورنالی
زبان: English
View: 50
This Paper With 14 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_CEJ-8-7_015
تاریخ نمایه سازی: 1 اردیبهشت 1403
Abstract:
In many cases, the repair strategy by using sacrificial anodes for cathodic protection in real RC structures requires additional zinc anodes after several years due to the decreasing protective area. This experimental study evaluates the effectiveness of time lag application of sacrificial anode cathodic protection applied to RC beam specimens that deteriorated severely due to chloride attack. In the experiment, sacrificial anodes and cathodic protection (SACP) were applied to ۴۱-year-old RC beam specimens exposed to natural marine environments in which the embedded steel bars were significantly corroded. The repair work was performed in three stages. Instant-off and rest potential tests of steel bars were conducted periodically to demonstrate the time-dependent depolarization value. In the first stage, a polymer-modified mortar as a patch repair material was cast to replace the concrete in the middle tensile part with small sacrificial anodes embedded in the mortar. After the protective current reaches an equilibrium state, the sacrificial anodes are disconnected from the steel bars for a year, defined as the second stage. During the one year in the second stage, the steel bar in the patch repair area remained passive, without any sign of corrosion. As for the third stage, additional sacrificial anodes were installed in the existing concrete part to protect the steel in it. From one year of observation after applying sacrificial anodes to old concrete parts, the time lag SACP application of both in patch and non-patch repair parts was clarified to be effective in stopping the corrosion of steel bar in both parts until ۲۰–۳۰ years based on the service life prediction. Doi: ۱۰.۲۸۹۹۱/CEJ-۲۰۲۲-۰۸-۰۷-۰۱۵ Full Text: PDF
Keywords:
Patch Repair , Sacrificial Zinc Anode , Service Life , Steel Corrosion , Time Lag Cathodic Protection.
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :