Effect of the Mortar Volume Ratio on the Mechanical Behavior of Class CI Fly Ash-Based Geopolymer Concrete
Publish place: Civil Engineering Journal، Vol: 8، Issue: 9
Publish Year: 1401
نوع سند: مقاله ژورنالی
زبان: English
View: 72
This Paper With 16 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_CEJ-8-9_012
تاریخ نمایه سازی: 1 اردیبهشت 1403
Abstract:
This research described the effect of the mortar volume ratio on the mechanical behavior of Class CI fly ash-based geopolymer concrete. The absolute volume ratio parameters were designed to determine the effects on the mechanical properties of the geopolymer concrete. The volume ratio of the mortar to coarse aggregate voids (Rc) was increased by ۰.۲۵ increments, from ۱ to ۱.۷۵, using constant parameters of ۱۰ M NaOH at a ratio of Na۲SiO۳to NaOH (R). Furthermore, the alkaline to fly ash ratio (A) of ۰.۳۵ and the volume ratio of paste to fine aggregate voids (Rm) of ۱.۵ were based on geopolymer paste and mortar investigations previously published. The test results showed that ۱) the Rc ratio influences the workability and compressive strength of geopolymer concrete; ۲) the increase in the Rc ratio by ۱.۷۵ is not linear with the rise in compressive strength but produces better mechanical properties; ۳) it does not affect the tensile strength of both geopolymer and OPC concretes; ۴) the lower the Rc ratio, the higher the flexural strength; ۵) the Rc ratio does not affect the OPC concrete and GC tensile strength; ۶) the bond stress in geopolymer concrete with an Rc ratio of ۱.۷۵ is higher than in OPC concrete; and ۷) Rc ratio does not affect the early strength of geopolymer concrete. The geopolymer concrete experienced an increase in compressive strength after ۲۸ days, while the OPC concrete remained flat. The results will help develop an optimal mix design of Class CI fly ash with moderate calcium oxide in the production of geopolymer concrete. This will improve the future applications of using this process in new binding materials. Doi: ۱۰.۲۸۹۹۱/CEJ-۲۰۲۲-۰۸-۰۹-۰۱۲ Full Text: PDF
Keywords:
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :