Effect of Multiaxiality on the Stress Rupture Properties of P۹۲ Steel
Publish Year: 1403
نوع سند: مقاله ژورنالی
زبان: English
View: 58
This Paper With 7 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMSEI-21-2_009
تاریخ نمایه سازی: 14 مرداد 1403
Abstract:
High thermal conductivity, low coefficient of thermal expansion makes P۹۲ a candidate material for Ultra Super Critical (USC) power plant piping. Microstructural features viz., high dislocation density, lath martensitic microstructure, fine precipitates of M۲۳C۶ and MX (X=C, N) contribute towards the high rupture strength. However, most components are typically subjected to multiaxial stress conditions; either metallurgical (weldments), or mechanical (change in the dimension). The present work involves stress rupture testing of circumferential ۶۰° V- notch specimens in the range of ۳۰۰ – ۳۷۵ MPa at ۶۵۰ °C. Notch strengthening effect was observed; with rupture times ranging from ۲۰۰ – ۱۳۰۰ h. Scanning electron microscopy (SEM) fractography revealed mixed mode of fracture with brittle fracture observed at notch root, while ductile fracture was seen at the centre of the specimen.
Keywords:
Authors
lakshmiprasad maddi
Department of BSHGMRIT
Srinivas R Gavinola
Department of Physics, Presidency University, Yelahanka, Bengaluru, Karnataka, INDIA, ۵۶۰۰۶۴.
Atul Ballal
Department of Metallurgical and Materials Engineering, Visvesvaraya National Institute of Technology, Nagpur, Maharashtra, INDIA, ۴۴۰۰۱۰.
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :