Fabrication of a (Ti,Hf)-Rich NiTiHf Alloy Using Graphitic Mold and Crucible
Publish Year: 1390
نوع سند: مقاله کنفرانسی
زبان: English
View: 983
This Paper With 6 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICME12_021
تاریخ نمایه سازی: 25 شهریور 1392
Abstract:
In this research, fabrication of a (Ti,Hf)-rich NiTiHf by using VIM process and a graphitic crucible was investigated. For this purpose, several casts with nominal composition of Ni49Ti36Hf15 were prepared in graphitic crucible and mold. OM, SEM, EDS, XRD, and DSC tests were employed to characterize the samples. Results demonstrated that microstructure of the first cast was composted of a B2 austenite phase as well as a great amount of two differently formed (Ti,Hf)C carbides. Moreover, no austenite ↔ martensite transformation peak was detected in DSC curve of this sample, indicating the drastic decline of the transformation temperatures. In the succeeding casts, however, owing to the formation of carbide layers on the inner surfaces of the graphitic crucible and mold during the initial casting process, the amounts of carbides remarkably decreased. These casts exhibited transformation temperatures above 100 ºC in DSC curves, while XRD pattern denoted the presence of B19´ monoclinic martensite phase at room temperature. All in all, results confirmed that VIM process using graphitic mold and crucible can be considered as an appropriate method for fabrication of (Ti,Hf)-rich NiTiHf high temperature shape memory alloys.
Keywords:
Carbide , High temperature shape memory alloy , Martensite , Microstructure , NiTi , Transformation temperatures
Authors
M Moshref-Javadi
School of Materials & Metallurgical Engineering, Iran University of Science & Technology, Tehran, Iran
M Belbasi
School of Materials & Metallurgical Engineering, Iran University of Science & Technology, Tehran, Iran
S. H. Seyedein
School of Materials & Metallurgical Engineering, Iran University of Science & Technology, Tehran, Iran
M. T. Salehi
School of Materials & Metallurgical Engineering, Iran University of Science & Technology, Tehran, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :