Effect of baria on γ-Al2O3 phase transition temperature and sintering
Publish place: 07th International Congress on Chemical Engineering
Publish Year: 1390
نوع سند: مقاله کنفرانسی
زبان: English
View: 680
This Paper With 8 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICHEC07_346
تاریخ نمایه سازی: 25 فروردین 1394
Abstract:
In the present study the effect of Ba2+ cation on the γ-Al2O3 to α-Al2O3 phase transition and sintering have been considered by differential thermal analysis and Scanning electron microscopy. For this purpose first γ-Al2O3 was synthesized from pseoudo boehmite and then Ba2+ was added by impregnation using barium nitrate solution, to γ-Al2O3 surface and γ-Al2O3 modified with 0.1, 1, 3, 5, 10 wt% of baria to find the optimum Ba2+ content for preventing γ-Al2O3 from phase transition and sintering.
Keywords:
Authors
Hoda Safaee
Corresponding Author’s Address: Chemical Engineering Department, Amirkabir University of Technology,Hafez Avenue, P.O. Box ۱۵۸۷۵-۴۴۱۳, Tehran, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :