Morphology and Properties of PVC/Clay Nanocomposites with enhanced Tensile properties
Publish place: 07th International Congress on Chemical Engineering
Publish Year: 1390
نوع سند: مقاله کنفرانسی
زبان: English
View: 806
This Paper With 6 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICHEC07_467
تاریخ نمایه سازی: 25 فروردین 1394
Abstract:
Behavior of Poly(vinyl chloride) (PVC) nanocomposites containing nanofillers, such as nanoclay (Cloisite 30B) were investigated. Samples were prepared with the nano content 3, 5, 7, 10 (phr) and their mechanical properties such as Tensile Strength, Tensile Modulus have been considered.Tensile strength and deflection at break also increased with increasing Clay loading.Scanning Electron Microscopy (SEM) data and Wide Angle X-Ray Diffraction(WAXD) were in support of the formation of partially delaminated nanocomposite material
Keywords:
Authors
m.k Pirzadeh Shahnani
Islamic Azad University Mahshahr Branch, Polymer Engineering Department, Mahshahr
p Soleimani Hamidy Nejad
Malek AshtarUniversity Esfahan Branch, Chemistry Department, Esfahan, Iran
s Zamirian
Islamic Azad University Darab Branch, Polymer Engineering Department, Darab, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :