Investigation of TiO2 Pigment Dispersion in ABS Matrix Using Rheological Parameters
Publish place: 07th International Congress on Chemical Engineering
Publish Year: 1390
نوع سند: مقاله کنفرانسی
زبان: English
View: 601
This Paper With 6 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICHEC07_533
تاریخ نمایه سازی: 25 فروردین 1394
Abstract:
At oscillatory rheometry method in linear viscoelastic region, storage and loss modulus vs.frequency graph of ABS at molten state has two crossover points (COP). First COP increases while TiO2 content arises up to 1.5% in Cristal 134 pigmented ABS samples. By arising TiO2 firstCOP dramatically decreases because of agglomeration of the pigments. TEM micrographs approve that agglomerates of Cristal 134 particles are formed above 1.5% content. Therefore, shifting of first COP as a rheological parameter could be applied as a criterion to specify dispersion quality of TiO2 particles in ABS matrix
Keywords:
Authors
Soheil Farshbaf Taghinejad
Iran Petrochemical and Polymer Institute, Tehran, Iran.
Mina Behrouzi
National Petrochemical Company (NPC), Research and Technology Company, Tehran, Iran..
Saeed Asiaban
National Petrochemical Company (NPC), Research and Technology Company, Tehran, Iran..
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :