Microstructure and Grain Refining Performance of a New type of Al-Ti-C master alloy
Publish place: 3rd Iran International Aluminium Conference (IIAC2014)
Publish Year: 1393
نوع سند: مقاله کنفرانسی
زبان: English
View: 613
This Paper With 5 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IIAC03_009
تاریخ نمایه سازی: 9 فروردین 1395
Abstract:
Grain refining process plays a significant role in preventing columnar and coarse grains and it encourages fine grain formation. Although Al–Ti–B master alloys use widely as aluminium grain refiners, but there are several problems in their applications. So, this kind of master alloys use less than last. Because of great properties of Al–Ti–C refiners, they can be considered as suitable candidates for use instead of Al–Ti–B master alloys. In recent years, Al–Ti–C refiners have attracted huge attention among researchers. In this paper, Al-3Ti-1C master alloy prepared with a melting reaction method. This method involves adding graphite powder and fine titanium particles into super-heated pure aluminium. Then microstructure of this master alloy studied by scanning electron microscope (SEM) and its phases distinguished by energy dispersive spectroscopy (EDS). In the next part, 200 ppm of Al-3Ti-1C master alloy added to pure aluminium and its refining efficiency compared with the condition in which TiC powders added to aluminium melt directly. It found that the fading time for both Al-3Ti-1C and TiC powder is about 15 minutes and in overall, grain refining efficiency of Al-3Ti-1C is more than TiC powders in 60 minutes
Keywords:
Authors
Vahid Hassanbeygi
Department of Materials Engineering, Isfahan University of Technology, Isfahan, Iran
Ali Shafyei
Department of Materials Engineering, Isfahan University of Technology, Isfahan, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :