An investigation on microstructure properties of Al6061/Al2O3 nanocomposite in as-cast state and in extruded condition
Publish place: 3rd Iran International Aluminium Conference (IIAC2014)
Publish Year: 1393
نوع سند: مقاله کنفرانسی
زبان: English
View: 748
This Paper With 8 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IIAC03_044
تاریخ نمایه سازی: 9 فروردین 1395
Abstract:
Al6061 reinforced with the hard particles, have higher strength, stiffness and wear and creep resistance than their unreinforced alloys in a wide temperature range and can be used for automotive components and aircraft structures. In the present work, Al6061/nano-Al2O3 composites were fabricated by stir-casting process through injection of Al2O3 particles into the molten Al alloy by the argon gas along with stirring using a mechanical stirrer, followed by extrusion at 550°C. The effects of adding nanoparticles (Al2O3) and extrusion process on the microstructure properties of the composites were investigated. The results show that Al2O3 nanoparticles are reasonably distributed in the matrix alloywith low agglomeration and porosity. Al2O3 particulates were distributed in the inter grains, with some particulates locating in grains. Also nanoparticles effectively caused to decrease grain size of matrix.
Keywords:
Authors
Hamid Reza Ezatpour
Department of Materials Science and Metallurgical Engineering, Engineering Faculty, Ferdowsi University of Mashhad, Mashhad, Iran
Seyed Abolkarim Sajjadi
Department of Materials Science and Metallurgical Engineering, Engineering Faculty, Ferdowsi University of Mashhad, Mashhad, Iran
Mohsen Haddad Sabzevar
Department of Materials Science and Metallurgical Engineering, Engineering Faculty, Ferdowsi University of Mashhad, Mashhad, Iran
Yizhong Huang
School of Materials Science and Engineering, Nanyang Technological University, Singapore 639798, Singapore.
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :