The effect of crosslinking temperature upon density and swelling degree of PDMS and PES membranes
Publish Year: 1395
نوع سند: مقاله کنفرانسی
زبان: English
View: 644
This Paper With 7 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
CHCONF02_124
تاریخ نمایه سازی: 9 مرداد 1395
Abstract:
In this research beneficial of PDMS (poly dimethylsiloxane) and PES (poly ether sulfonic) membranes with crosslinking TEOS (tetra ethyl ortho silicate) as silica Nano particles, ammonia as catalyst/inducer, and span 80 as surfactant. In this research, variation of crosslinking temperature (T), from 65-85 Ċ upon density (ρp), swelling degree (MsD) and %swelling by volume, is studied. It was observed that with increase the crosslinking temperature, ρp is increased and MsD , %swelling by volume is decreased.
Keywords:
Authors
Mohsen Farsi
Department of chemical engineering, science and Research Branch, Islamic Azad university, Tehran, Iran
Amir Heidarinasab
Department of chemical engineering, science and Research Branch, Islamic Azad university, Tehran, Iran
Bizhan Honarvar
Department of chemical engineering, Marvdasht Branch, Islamic Azad university, Marvdasht , Iran
Mehdi Arjmand
Department of chemical engineering, science and Research Branch, Islamic Azad university, Tehran, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :