Effect of aramid pulp fibers and irradiated Polytetrafluoroethylene ( PTFE) on mechanical properties of Polyamide 6
Publish place: دهمین سمینار بین المللی علوم و تکنولوژی پلیمر
Publish Year: 1391
نوع سند: مقاله کنفرانسی
زبان: English
View: 318
متن کامل این Paper منتشر نشده است و فقط به صورت چکیده یا چکیده مبسوط در پایگاه موجود می باشد.
توضیح: معمولا کلیه مقالاتی که کمتر از ۵ صفحه باشند در پایگاه سیویلیکا اصل Paper (فول تکست) محسوب نمی شوند و فقط کاربران عضو بدون کسر اعتبار می توانند فایل آنها را دریافت نمایند.
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ISPST10_399
تاریخ نمایه سازی: 6 اردیبهشت 1396
Abstract:
Today, polyamide 6 (PA6)-reinforced polymeric materials are widely used as structural materials, and there is a growing interest in both commercial and scientific matters because oftheir advantages in engineering composites such as tribological applications[1]. To improve the stiffness andstrength of the polymeric materials, fillers in the form of particulates and fibers are often added to them. Aramid pulp is a short, tough, highly fibrillated aramid fiber with suitable properties such as high wear resistance and high fatigue life, and good compatibility to be used in PA6 matrices [2-3]. Ashort-fiber reinforced system has higher degree of low-strain reinforcement compared to particulate–filler composites even at relatively low-fiber content [3]. On the other hand, extraordinary characteristics of Polytetrafluoroethylene (PTFE) such as very low friction coefficient, good hightemperature stability and chemical stability are very appealing in tribological applications. PTFE is innately a lowfrictionand inert material with low adhesion to polymeric matrices. Therefore, it is electron-beam irradiated to improve compatibility and dispersion in polymeric matrixes such asPA6 [4]. In this work, mechanical properties of polyamid 6/ aramid pulp fiber with Nano-size branches and polyamid 6/ Irradiated Polytetrafluoroethylene (PTFE) composites were investigated in order to produce a suitable composite for engineering composites for tribological applications.
Authors
Iraj Faramarzi
Polymer Engineering Department, Faculty of Chemical Engineering, Tarbiat Modares University
Mehdi Razzaghi-Kashani
Polymer Engineering Department, Faculty of Chemical Engineering, Tarbiat Modares University
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :