Nanofiber scaffolds from PCL/ Poly(amidoamine) dendrimers
Publish place: International Conference/Workshop of Inter-Islamic Network on Nanotechnology (INN) on Nanotechnology and Nanomedicine
Publish Year: 1396
نوع سند: مقاله کنفرانسی
زبان: English
View: 728
متن کامل این Paper منتشر نشده است و فقط به صورت چکیده یا چکیده مبسوط در پایگاه موجود می باشد.
توضیح: معمولا کلیه مقالاتی که کمتر از ۵ صفحه باشند در پایگاه سیویلیکا اصل Paper (فول تکست) محسوب نمی شوند و فقط کاربران عضو بدون کسر اعتبار می توانند فایل آنها را دریافت نمایند.
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
NTNM01_044
تاریخ نمایه سازی: 7 اسفند 1396
Abstract:
We report a facile and effective approach to use generation 2 (G2) poly(amidoamine) (PAMAM) dendrimers for functionalization of poly(ε-caprolactone). In this approach, the PAMAM dendrimer was directly used as an aminolysis agent in PCL dope solution for the functionalization of PCL in one step process. We investigated effect of two parameters of concentration denderimer and time of the dope on the morphology electrospun nanofiber. Addition of denderimer to the polymer solution resulted in aminolysis of PCL. With increasing time at Constant temperature the aminolysis increased. This was clearly observed when nanofibers were fabricated. The diameter of nanofiber prepared from solution left for 1h was 351nm whereas the diameter of nanofibers prepared from Solution left for 3h reduced to 179 nm. The amount of dendrimer added to the polymer dope also affected the diameter of nanofibers. With increasing denderimer concentration the nanofiber diameter decreased.
Keywords:
Poly(ε-caprolactone) (PCL); Poly(amidoamine) (PAMAM) dendrimers; Electrospinning; Aminolysis
Authors
Pouyan Razmshoar
Textile Engineering Department, Amirkabir University of Technology, Tehran, Iran
S.Hajir Bahrami.
Textile Engineering Department, Amirkabir University of Technology, Tehran, Iran
Somaye Akbari.
Textile Engineering Department, Amirkabir University of Technology, Tehran, Iran