Enhancing the performance of polysulfone ultrafiltration membranes by mixing with polyacrylic acid for canal water treatment
Publish place: Advanced Journal of Chemistry-Section A، Vol: 1، Issue: 1
Publish Year: 1397
نوع سند: مقاله ژورنالی
زبان: English
View: 279
This Paper With 10 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_AJCS-1-1_003
تاریخ نمایه سازی: 20 مهر 1398
Abstract:
We developed some Ultrafiltration (UF) membranes based on polysulfone (PSF) and poly acrylic acid (PAA) mixture. The Ultrafiltration membraneswere prepared by the phase inversion technique using Dimethylformamide (DMF) as a solvent. Immobilization of PAA in PSF matrix was confirmed by Fourier transform infrared spectroscopy (FTIR). The membranes have an asymmetric structure, as revealed by scanning electron microscopy (SEM). Natural water from Mahmoudia canal (a subdivision of the Nile River) is used as feed water. The permeate flux reached 120.0 l/m2.hr. The hydrophilicity measured by contact angle was enhanced by the addition of PAA to reach 66.00. The prepared membranes showed good tensile strength that reached 7.2 MPa. Turbidity rejection and dissolved organic carbon (DOC) rejection reached 98.4% and 65 %, respectively. These performances obtained at ambient operating conditions, make the fabricated membranes attractive for canal water treatment.
Keywords:
Authors
Mohamed Abdel Aal
Department of chemistry, Faculty of Science, Alexandria University,Egypt.
Abdel Monem Ahmed
Department of Chemistry, Faculty of Science, University of Alexandria, Alexandria, Egypt
Hanaa Abdel Rahman
Department of Chemistry, Faculty of Science, University of Alexandria
Sherif Kandil
Professor of Physical Chemistry of Materials, Material Science Department, Institute of Graduate Studies &Research, University of Alexandria
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :