Influence of Notch Depth-to-Width Ratios on J-Integral and Critical Failure Load of Single-Edge Notched Tensile Aluminium 8011 Alloy Specimens
Publish place: Journal of Solid Mechanics، Vol: 10، Issue: 1
Publish Year: 1397
نوع سند: مقاله ژورنالی
زبان: English
View: 301
This Paper With 12 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JSMA-10-1_006
تاریخ نمایه سازی: 12 اسفند 1398
Abstract:
In this paper, the influence of notch depth-to-width ratios on J-integral and critical load of Aluminium 8011 alloy specimens with U-notch under Mode I loading are studied. Using experiments, for a set of specimens having different notch depth–to–width ratios, J-integral was found and the same was verified using analytical methods. Further, using the results obtained from the experiments, failure assessment diagrams (FAD) were plotted for the same ratios, to determine the safe or critical load and the type of failure mechanism was also studied. The results show that, for both shallow and deep notch depths, the J-integral values obtained from the experimental method, are in very close agreement with the analytical values. J-integral values decrease with increase in notch depth and increase with increase in applied load. Furthermore, from FAD, the safe load decreases when the notch depth-to-width ratio increases and it was found that, all the tested specimens failed due to elastic plastic deformation mechanism.
Keywords:
Authors
C.S Sumesh
Department of Mechanical Engineering, Amrita School of Engineering, Coimbatore Amrita Vishwa Vidyapeetham, India
P.J Arun Narayanan
Department of Mechanical Engineering, Amrita School of Engineering, Coimbatore Amrita Vishwa Vidyapeetham, India
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :