Nano recrystallization during severe plastic deformation of AZ31 magnesium alloy
Publish place: 1st International and 6th Joint Conference of Iranian Society of Metallurgical Engineers and the scientific community of Casting
Publish Year: 1391
نوع سند: مقاله کنفرانسی
زبان: English
View: 1,247
This Paper With 10 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IMES06_324
تاریخ نمایه سازی: 8 بهمن 1391
Abstract:
The present investigation has been conducted to clarify the formation mechanisms of nano structures in an accumulative back extruded (ABEed) AZ31 magnesium alloy. Thedeformation pattern involved in the accumulative back extrusion (ABE) is mainly controlled by shear bands formation. This was accompanied by cell structure development which subsequently transformed to equiaxed ultrafine and nano-sized grains. Moreover, it was foundthat transverse boundaries had segmented the nano twins into regions of ultra-fine and nanoscale size.
Authors
S.M Fatemi-Varzaneh
School of Metallurgy and Materials Engineering, University of Tehran, Tehtan, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :