In Situ Formation of SiC/CNT Ceramic Nanocomposite by Phenolic Pyrolysis
Publish place: Mechanics of Advanced Composite Structures، Vol: 1، Issue: 2
Publish Year: 1393
Type: Journal paper
Language: English
View: 322
This Paper With 10 Page And PDF Format Ready To Download
- Certificate
- I'm the author of the paper
Export:
Document National Code:
JR_MACS-1-2_003
Index date: 4 July 2020
In Situ Formation of SiC/CNT Ceramic Nanocomposite by Phenolic Pyrolysis abstract
In this research, using pyrolysis of phenolic resin in the presence of silicon particles, the SiC ceramic composite is formed. The samples were prepared by introducing 30, 35, 40, 45 and 50 wt% of Si particles to the phenolic resin. The samples were cured at 180°C then carbonized at 1100°C. The final carbonized C/Si composites are hot-pressed at 1500°C in inert atmosphere, which is more than the melting point of Si particles. In this temperature, Carbon vapor and melted Si react and SiC ceramic is formed. The XRD analysis of samples showed that SiC peak was observed in the final product while carbonized phenolic and Si particles also existed in the matrix. The samples were so brittle and therefore, several impregnation processes should have been used to reduce the porosity of composite. SEM images of in situ composite reveal extraordinary phenomenon which is related to the formation of CNT and nanostructures on the base of Si particles that grow like flower in the matrix. These nanostructures are one of the reasons for higher mechanical properties of final nanocomposite. Three-point flexural tests are also conducted for better understanding of mechanical improvement.
In Situ Formation of SiC/CNT Ceramic Nanocomposite by Phenolic Pyrolysis Keywords:
In Situ Formation of SiC/CNT Ceramic Nanocomposite by Phenolic Pyrolysis authors
Hamid Salehi
Department of Mechanical Engineering, Amirkabir University of Technology, Tehran, Iran
Manouchehr Salehi
Department of Mechanical Engineering, Amirkabir University of Technology, Tehran, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :