Effect of resistance spot welding parameters on microstructure and mechanical properties of 1050 aluminium alloy and ST14 carbon steel joint

In this study, the connection of 1050 aluminum alloy to St14 plain carbon steel was investigated by point resistance welding method. The variable parameters in this processwere the holding time of the jaws and the power of the device. After welding, shear tests, microstructure and microhardness tests were performed. Examination of EDS analysis in the welding zone showed that the compounds formed near the steel layer are mainly ironrich intermetallic compounds and in the part near the aluminum alloy the intermetallic compounds are richer than aluminum. The results of shear test showed that the highest shear strength was related to the connected sample with a power of 2.5 kV and a duration of 7 seconds in the amount of 116.60 MPa and the lowest shear strength was related to the connected sample with a power of 2.5 kV and a duration of 4 The second was 19.80 MPa. The results of the microhardness test showed that the highest amount of microhardness in the welding button was related to the sample connected in 4 seconds and the power of 2.5 kW was 240.57 Vickers and the lowest amount of microhardness was related to the sample. Connected in 5 seconds and a power of 7.5 kW was 165.57 Vickers. Keywords: Point Resistance Welding (RSW), 1050 Aluminum, ST14 Steel.

Keywords:

Resistance Spot Welding , 1050 Alumimium Alloy , St14 Steel.