Effect of graphene nanoplatelets on the microstructure and mechanical behavior of erbium-modified Al-۷.۵Si-۰.۵Mg alloy
Publish place: Journal of Particle Science & Technology، Vol: 6، Issue: 1
Publish Year: 1399
نوع سند: مقاله ژورنالی
زبان: Persian
View: 203
This Paper With 9 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JPST-6-1_004
تاریخ نمایه سازی: 5 اردیبهشت 1400
Abstract:
In this study, the effects of adding erbium and graphene (separately and in combination) on the microstructure and mechanical properties of Al-۷.۵Si-۰.۵Mg alloy were investigated. Initially, the primary alloy was produced by casting in the form of ingots. To add graphene to the molten alloy, these particles were milled with aluminum powder for ۳ h. Then ۰.۲, ۰.۴, and ۰.۶ wt% graphene, ۰.۲ wt% erbium, and finally, a combination of ۰.۲ wt% erbium with ۰.۴ wt% graphene were incorporated into the Al-۷.۵Si-۰.۵Mg alloy. The microstructure of the produced samples was examined using optical and electron microscopes, then the tensile and wear behaviors of the produced samples were examined. Finally, scanning electron microscopy (SEM) images were used to investigate the mechanisms of wear and failure. The results of this study showed that the addition of erbium and graphene modified the microstructure of the alloy and reduced the grain size of the alpha-aluminum. The best tensile and wear properties were obtained for the sample containing ۰.۲ wt% erbium + ۰.۴ wt% graphene. By adding this value to the Al-۷.۵Si-۰.۵Mg alloy, tensile strength and wear resistance were increased by ۵۶% and ۶۷%, respectively, compared to the control sample.
Keywords:
Authors
Seyed Masoud Alavi
Department of Materials Engineering, Faculty of Engineering, University of Sistan and Baluchestan, Zahedan, Iran
Hamed Khosravi
Department of Materials Engineering, Faculty of Engineering, University of Sistan and Baluchestan, Zahedan, Iran
Esmaeil Tohidlou
Department of Materials Engineering, Faculty of Engineering, University of Sistan and Baluchestan, Zahedan, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :