A Kinetic Study of Vanadium Dissolution During Acetic Acid Leaching of Steel Making Converter Slag
Publish Year: 1399
نوع سند: مقاله ژورنالی
زبان: English
View: 165
This Paper With 10 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JMATPR-8-4_004
تاریخ نمایه سازی: 9 مرداد 1400
Abstract:
Steelmaking slags are known as the secondary product of steel making process. Regarding the high rate of slag production and the existence of a noticeable amount of toxic and valuable metals such as vanadium in this material; recovery of vanadium from this product is necessary. In this study, steel making converter slag (containing about ۱.۹۶ wt.% V۲O۵) was ground to a mean size of ۸۵ µm, and recovery of vanadium was carried out using acetic acid leaching. The effects of time (in the range of ۰ to ۱۲۰ min) and temperature (in the range of ۰ to ۸۰ ⁰C) in fixed acetic acid concentration (۱ molal) and solid to liquid weight ratio (one gram slag in ۲۰۰ ml) on the leaching process were investigated. The results showed that the increase in time and decrease of temperature (activation energy was equal to -۱۱.۴ kJ/mol) increases vanadium leaching efficiency. Maximum leaching efficiency was reached at ۰ ⁰C and ۹۰ min. Kinetics studies showed that heat diffusion through the solid layer is the controlling step of vanadium dissolution in acetic acid. Furthermore, thermal conductivity (ka) decreases by increasing temperature (ka=۲۱۸۷۷.۶/T۳), so the heat moves away from the reaction zone to the particle's surface at a slower rate.
Keywords:
Authors
Seyed Amirhossein Emami
Advanced Materials Research Center, Department of Materials Engineering, Najafabad Branch, Islamic Azad University, Najafabad, Iran
Mohammad Reza Kelishadi
Advanced Materials Research Center, Department of Materials Engineering, Najafabad Branch, Islamic Azad University, Najafabad, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :