Synthesis of Nanostructured MnNiAPSO-۳۴ Catalyst: Catalytic Properties and Performance
Publish Year: 1393
نوع سند: مقاله ژورنالی
زبان: English
View: 144
This Paper With 18 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JMATPR-2-2_006
تاریخ نمایه سازی: 12 مهر 1400
Abstract:
Silicoaluminophosphate (SAPO-۳۴) molecular sieve doped with transition metals, Mn and Ni, with different molar ratios (Mn/Ni=۰.۳۳, ۳) were investigated for their activity, selectivity and lifetime in biomethanol to olefins reaction. MnNiAPSO-۳۴ nanostructured catalyst was synthesized by hydrothermal method and addition of metals was carried out by isomorphous substitution into the crystalline framework of SAPO-۳۴. The nanostructured catalysts were characterized by XRD, FESEM, PSD, EDX, BET and FTIR techniques. MnNiAPSO-۳۴ nanostructured catalyst synthesized with high concentration of Mn, demonstrated larger crystallite size evidenced by XRD analysis. The FESEM results indicated that the concentration of metal ions could affect the morphology of nanostructured MnNiAPSO-۳۴ catalyst due to different rate of crystal growth. The catalytic performance of samples was studied in biomethanol to olefins reaction at atmospheric pressure and GHSV of ۴۲۰۰ cm۳/g.h-۱ in a fixed bed reactor. MnNiAPSO-۳۴ with high concentration of Mn illustrated higher selectivity toward light olefins and had longer lifetime for which the selectivity of light olefins for this nanostructured catalyst was ۶۰% after ۱۸۰ min time on stream.
Keywords:
Authors
Parisa Sadeghpour
Chemical Engineering Faculty, Sahand University of Technology, Sahand New Town, Tabriz, Iran. Reactor and Catalysis Research Center (RCRC), Sahand University of Technology, Sahand New Town, Tabriz,Iran
Mohammad Haghighi
Chemical Engineering Faculty, Sahand University of Technology, Sahand New Town, Tabriz, Iran. Reactor and Catalysis Research Center (RCRC), Sahand University of Technology, Sahand New Town, Tabriz,Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :