Silicothermic production and characterization of FeSiNi/SiO۲ Magnetic nanocompsite via mechanical alloying
Publish Year: 1393
نوع سند: مقاله ژورنالی
زبان: English
View: 164
This Paper With 6 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JMATPR-2-4_006
تاریخ نمایه سازی: 12 مهر 1400
Abstract:
In recent years, a lot of research has been done in the field of producing soft magnetic nano composites by means of mechanical alloying. These materials indicate more electrical resistance and permeability in comparison with soft magnetic composites (SMCs). In this research, reduction of silicothermal mixed powder (Nickel-oxide, Silicon and Iron) was carried out by mechanical alloying to form soft nano composites of FeSiNi/SiO۲. Scanning Electron Microscopy (SEM) and X-Ray Diffraction (XRD) were used to detect physical characterization and finding the effect of milling time on micro structural properties. It is determined that initiation of forming the homogenous alloy was in ۴ hour milling, increasing the time of milling to ۴۰ hours caused decreasing grain size to ۱۳ nm and formation of homogenous alloy. Magnetic properties of milled powder were studied by alternating gradient force magnetometer (AGFM) and it was observed that increasing milling time will cause improvement in soft magnetic properties (decreasing magnetic coercivity and increasing magnetic saturation).
Keywords:
Authors
Ghazal Sharifian asl
Department of Material Engineering, Najafabad Branch, Islamic Azad University, Isfahan, Iran
Ali Saidi
Department of Materials Engineering, Isfahan University of Technology, Isfahan, Iran