Investigation of Roll Bonding between AA۵۰۸۳ Strips
Publish Year: 1395
نوع سند: مقاله ژورنالی
زبان: English
View: 201
This Paper With 10 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JMATPR-4-3_004
تاریخ نمایه سازی: 12 مهر 1400
Abstract:
Layered alloys and composite materials have become an increasingly popular in industrial development. The roll bonding (RB) process, as a solid phase method of bonding, has been widely used in manufacturing large layered strips. In this study, aluminum alloy (AA ۵۰۸۳) strips were roll bonded at warm and cold temperatures. The effects of the rolling parameters such as the amount of plastic deformation by rolling and rolling temperature that create successful bonds on the bond strength and the threshold deformation between two layer strips of AA ۵۰۸۳/ AA ۵۰۸۳ were investigated. The bond strength was evaluated by the peeling test. It was found that by increasing the rolling temperature or thickness reduction, the peel strengths of the bonds increased and successful bonds with higher strength were created. Also, the threshold thickness reduction decreased with increasing the rolling temperature. Moreover, the interfaces of laminates were studied by scanning electron microscopy (SEM) in order to investigate the bonding quality.
Keywords:
Authors
Mohammad Sedighi
School of Mechanical Engineering, Iran University of Science and Technology, Tehran ۱۶۸۴۴, Iran
mohammad heydari vini
department of engineering, islamic azad university of mobarakeh branch, mobarakeh, isfahan, iran
Pedram Farhadipour
School of Mechanical Engineering, Iran University of Science and Technology, Tehran ۱۶۸۴۴, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :