The effect of partial Nb doping on magnetic and electrical behavior of Y-۱۲۳ superconductors with Nano CuO
Publish place: The Physics Society Of Iran، Vol: 21، Issue: 3
Publish Year: 1400
نوع سند: مقاله ژورنالی
زبان: Persian
View: 148
This Paper With 6 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_PSI-21-3_007
تاریخ نمایه سازی: 26 اردیبهشت 1401
Abstract:
We have investigated the effect of Niobium and Nano CuO (۴۰ nm) dopingY۱-xNbxBa۲Cu۳O۷-∂ compounds with ۰.۰۰ ≤ x ≤ ۰.۰۵ wt. %, prepared by the conventional solid-state method by means of XRD, SEM, R(T) and magnetic loops (MH) measurements. The critical current densities, Jc as a function of temperature have been calculated using the critical state model from the hysteresis loops up to ۱ kG at the temperature range of ۱۰-۶۰ K. Magnetic flux pinning, Fp of samples was calculated by using Lorentz force. The temperature dependence of the electrical resistivity measurement curves indicated that the sample with x=۰.۰۱ wt.% has a high transition temperature, Tc. XRD analysis shows a shorter c axis lattice parameter and higher orthoromthcity than the pure Y-۱۲۳ and other Nb-doped samples. It was also found from Jc and Fp measurement, that the ۰.۰۱ wt.% Nb substation for the Y on YBCO superconductor improves the Jc and Fp.
Keywords:
Authors
حسن صدقی
استاد-دانشگاه ارومیه
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :