High temperature acidic oxidation of multiwalled Carbon nanotubes and synthesis of Graphene quantum dots
Publish place: International Journal of Nano Dimension، Vol: 9، Issue: 2
Publish Year: 1397
نوع سند: مقاله ژورنالی
زبان: English
View: 108
This Paper With 7 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJND-9-2_009
تاریخ نمایه سازی: 22 خرداد 1401
Abstract:
The acid oxidation of carbon nanotube generally results in opening the close ends of the nanotube and to make surface modifications. Herewith, Multiwall carbon nanotubes (MWCNTs) were oxidized in acids at high temperature experimental conditions which led to the formation of graphene quantum dots (GQDs). High resolution transmission electron microscope (HRTEM), energy dispersive X-ray spectroscopy (EDS), IR Infrared study showed the formation of ۵-۱۰ nm diameter GQDs and their crystalline structure having the inter-planner distance of ۲.۴۰Å and ۲.۱۴Å was confirmed by the electron diffraction. The UV visible spectroscopy showed the lowest exciton peak at ۴eV. Photoluminescence (PL) studies showed the Photoluminescence peak in visible range which is independent of excitation wavelengths. A mechanism for the formation of highly crystalline graphene quantum dots during the high temperature acid oxidation of MWCNTs is proposed in the paper.
Keywords:
Authors
Neelam Kushwaha
Amity Institute of Nanotechnology, Amity University Uttar Pradesh, Noida, Uttar Pradesh, India, ۲۰۱۳۰۱.
Jagjiwan Mittal
Amity Institute of Nanotechnology, Amity University Uttar Pradesh, Noida, Uttar Pradesh, India, ۲۰۱۳۰۱.
Shifa Pandey
Amity Institute of Nanotechnology, Amity University Uttar Pradesh, Noida, Uttar Pradesh, India, ۲۰۱۳۰۱.
Robin Kumar
Amity Institute of Nanotechnology, Amity University Uttar Pradesh, Noida, Uttar Pradesh, India, ۲۰۱۳۰۱.
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :