Laboratory Evaluation of Electrical Resistance of Concrete
Publish Year: 1400
نوع سند: مقاله ژورنالی
زبان: English
View: 123
This Paper With 13 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JCEMA-6-2_004
تاریخ نمایه سازی: 27 آذر 1401
Abstract:
Common methods of controlling setting, hardness, process of strength concrete are tests for determining the setting time of mortar and concrete and determining the compressive strength of concrete It seems that these physical methods, do not fully reflect the behavior of concrete and the process of changing phase states during the hydration process; however, with the method of the electrical resistance of concrete, this observation is possible. Therefore, in this study, at the first stage, ۱۱ samples of cement were prepared, the phases of which varied, but due to laboratory cementation, their fineness and grading conditions were almost the same. Physical and chemical analysis of cement samples was performed. In the next step, ۲۲ concrete mixtures with ۱۱ cement samples were prepared, so that ۱۱ mixtures without additives and ۱۱ mixtures with constant dosage of commercial super plasticizer. Also in the all concrete mixtures, the slump kept constant about ۸ cm. Compressive strength tests of ۷, ۲۸ and ۹۰ days hardened concrete were performed on concrete mixtures. Also, an electrical resistance test was performed, which was performed regularly from the time of cement contact with water until ۳۱ days later. The results showed that at least three peaks of ۸, ۱۶ and ۲۳ days in the electrical resistance curve are seen along the test time. In almost all samples, the electrical resistance is reduced to about ۳ hours, which indicates the setting time of the concrete. Based on the results of this study, formula was presented.
Keywords:
Authors
Ali Akbar Kafash Bazari
Chief of research and development of Tehran cement Co, Tehran, Iran
Mehdi Chini
Assistant Professor of Road, Housing and Urban Development Research Centre, Tehran, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :