Multilayered PMMA Dental Material Reinforced with Electrospun PVP/ZrO۲ Composite Nanofiber Fabrics with Enhanced Flexural Properties
Publish Year: 1401
نوع سند: مقاله ژورنالی
زبان: English
View: 130
This Paper With 12 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JDMT-11-4_008
تاریخ نمایه سازی: 8 دی 1401
Abstract:
Introduction: This study presents a new design of multilayered PMMA dental composite material combining electrospun continuous composite polyvinylpyrrolidone (PVP) nanofibers filled with zirconia (ZrO۲) nanoparticles and two-component self-cure PMMA dental resin. The aim is to improve the mechanical properties of dental PMMA material via the large surface area of electrospun nanofibers, the toughening effect of PVP and ZrO۲ nanofillers. Methods: First, PVP/ZrO۲ composite nanofibers with different ZrO۲ contents of ۵%, ۱۰% and ۲۰% (wt. % of PVP) were prepared by electrospinning. Then, multilayered samples containing alternating PMMA resin and electrospun composite nanofiber mats with different ZrO۲ contents were manufactured by lay-up process. Samples containing single and double layers of nanofiber mats were prepared and cured in a water bath dental acrylic curing device in order to prepare composites without any void. Results: FTIR and SEM results reveal that PVP enables good interfacial interactions and compatibility between the nanofibers and PMMA matrix. The mechanical properties are improved as an increase of the flexural strength up to ۸۳% and ۶۷% is observed for PMMA/PVP/ZrO۲-۱۰s and PMMA/PVP/ZrO۲-۲۰d samples, respectively. The presence of PVP nanofiber layers significantly improves the flexural toughness, especially for samples reinforced with a single layer of nanofibers where improvements up to ۱۶۹% and ۱۵۳% are observed for PMMA/PVP/ZrO۲-۵s and PMMA/PVP/ZrO۲-۱۰s composite samples respectively. The micro-hardness is also higher for composite samples compared to neat PMMA dental material. Conclusion: The overall results clearly depict a noticeable enhancement of the mechanical properties, especially the flexural toughness of PMMA dental material
Keywords:
Authors
Serife Akkoyun
Department of Metallurgical and Materials Engineering, Faculty of Engineering and Natural Sciences, Ankara Yildirim Beyazit University, Ankara, Turkey
Mahmut Özdoğan
Department of Prosthodontics, Faculty of Dentistry, Ankara Yildirim Beyazit University, Ankara, Turkey
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :