EFFECT OF CRYSTALLIZATION TIME ON HYDROTHERMAL SYNTHESIS AND PHYSICOCHEMICAL CHARACTERIZATION OF CUO/ZNO/AL2O3 NANOPOWDER
Publish Year: 1391
نوع سند: مقاله کنفرانسی
زبان: English
View: 1,979
This Paper With 6 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICOGPP01_122
تاریخ نمایه سازی: 22 مرداد 1391
Abstract:
Hydrothermally synthesis of CuO/ZnO/Al2O3 nanopowder successfully carried out. The effect of crystallization time on product properties wasobserved and 6 h reaction time, based on powderXRD analysis and FESEM imaging, was selected as the best crystallization duration in range of 3-12 h.Nanopowders were characterized using XRD, FESEM, EDX mapping, FTIR, TG and BET techniques. The XRD patterns confirmed crystallinemetal oxide formation. Good crystallinity of samples was observed with FESEM image which confirmed XRD analysis results. Scherrer equation calculationsshowed average crystallite size of 20 nm for productsand FESEM images showed nano scale particles. The BES surface area measurement showed acceptablevalues for synthesized CZA samples. FTIR spectroscopy confirmed metal oxides formation during hydrothermal and calcination process. TGA results illustrated high thermal stability of the synthesized nanopowders
Authors
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :