EFFECT OF POST-DEFORMATION ANNEALING TREATMENT ON INTERFACE PROPERTIES AND SHEAR BOND STRENGTH OF Al-Cu BIMETALLIC RODS PRODUCED BY EQUAL CHANNEL ANGULAR PRESSING
Publish Year: 1396
نوع سند: مقاله ژورنالی
زبان: English
View: 131
This Paper With 10 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMSEI-14-4_003
تاریخ نمایه سازی: 24 مرداد 1402
Abstract:
Effects of annealing treatment after equal channel angular pressing (ECAP) on the interface properties and shear bond strength of Al/Cu bimetallic rods were investigated. For the as-deformed samples, the one with two passes of ECAP indicated higher shear bond strength. Formation of a layer of intermetallic compounds after annealing treatment is confirmed. In general, by increasing annealing temperature, thickness of intermetallic compounds at the interface increases. Shear bond strength was initially reduced by annealing at ۲۰۰, ۲۵۰ and ۳۰۰ ͦ C and increased at ۳۵۰ ͦ C. With further increase in annealing temperature to ۴۰۰ ͦ C, shear bond strength slightly decreased which is correlated to the increased thickness of the intermetallic compounds.
Keywords:
Authors
H. Mirzakouchakshirazi
Iran University of Science and Technology
A. Eivani
Iran University of Science and Technology
Sh. Kheirandish
Iran University of Science and Technology
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :