The Formation of Red Copper Glaze in an Oxidizing Atmosphere
Publish Year: 1402
نوع سند: مقاله ژورنالی
زبان: English
View: 65
This Paper With 9 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMSEI-20-3_003
تاریخ نمایه سازی: 11 شهریور 1402
Abstract:
This paper introduces a method for producing red copper glaze by adding copper oxide (CuO) and silicon carbide (SiC) additives to the base glaze. SiC created a reducing environment in situ and allowed the glaze to be sintered in an oxidizing furnace environment. Nanocrystals are the determinants of the red color of the glaze. The CuO reduction reaction temperature range of SiC produces a reducing environment in the glaze as detected by the method (DSC). The functional group and phase of nanocrystals were determined by Fourier transform infrared (FT-IR) and X-ray diffraction (XRD) spectroscopy.
Keywords:
Authors
Nguyen Vu Uyen Nhi
Ho Chi Minh City University of Technology (HCMUT)
Doan Duong Xuan Thuy
Ho Chi Minh City University of Technology (HCMUT)
Do Quang Minh
Ho Chi Minh City University of Technology (HCMUT)
Kieu Do Trung Kien
Ho Chi Minh City University of Technology (HCMUT),
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :