Using JMatPro Simulation to Study the Effect of Heat Treatment Temperature on the Dissolution of Gamma-Prime Phase in Inconel ۶۱۷ Nickel-Based Superalloy
Publish place: The Iranian Journal of Materials Forming، Vol: 10، Issue: 2
Publish Year: 1402
نوع سند: مقاله ژورنالی
زبان: English
View: 147
This Paper With 11 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMF-10-2_006
تاریخ نمایه سازی: 14 شهریور 1402
Abstract:
In this study the effect of heat treatment temperature on the formation and dissolution of gamma-prime phase has been studied in Inconel ۶۱۷. Since the working temperature of Inconel ۶۱۷ is above ۵۴۰°C, the samples were heat treated at different temperatures in a range between ۵۵۰ to ۸۵۰°C and simulations were performed at the same temperatures by the JMatPro software. It was found that the gamma-prime phase with different percentages (below ۱۰%) would exist in the temperature range of ۵۵۰ to ۸۰۰°C. However, it would gradually decrease as the temperature increases and finally dissolve completely at temperatures over ۸۰۰°C. The observations by metallography were in good agreement with the predictions made by the JMatPro software. The microstructure investigations using the optical and field emission electron microscopy showed that the gamma-prime phase exists at ۶۵۰°C and ۷۵۰°C, but its weight percent decreases with increasing temperature, so that at ۸۵۰°C no gamma-prime can be detected.
Keywords:
Authors
E. Asghari
Department of Materials Engineering, Faculty of Engineering, Yasouj University, Yasouj, Iran
R. Hayati
Department of Materials Engineering, Faculty of Engineering, Yasouj University, Yasouj, Iran
A. Momeni
Department of Materials Engineering, Faculty of Engineering, Hamedan University of Technology, Hamedan, Iran
N. Setoudeh
Department of Materials Engineering, Faculty of Engineering, Yasouj University, Yasouj, Iran
A. Mohassel
Department of Materials Engineering, Faculty of Engineering, Yasouj University, Yasouj, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :