The effect of quenching media and annealing temperature on graphitization transformation kinetic of CK۱۰۰ tool steel
Publish Year: 1390
نوع سند: مقاله ژورنالی
زبان: English
View: 47
This Paper With 5 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ISSIRAN-8-1_006
تاریخ نمایه سازی: 6 آبان 1402
Abstract:
In this research, graphitization transformation of a commercial hypereutectoid steel called CK۱۰۰ was studied by the dilatometric experiments at the range of ۶۰۰ – ۷۰۰ °C from prior martensitic structure. Also the effect of quenching media on the initial graphitization time and completion of transformation has been discussed. Also, graphitization transition from the different prior microstructures was studied using microscopic observations. Analyzing dilatometric data acquisitions confirmed good following results from Johnson–Mehl–Avrami equation. By calculating Avrami exponent, following of transformation kinetic from diffusion controlled nucleation and growth was resulted. Also, the minimum time for completion graphitization transformation was concluded about ۴۵ hrs relative to the water quenched specimen after annealing at ۶۷۰ °C.
Keywords:
Authors
S. Rounaghi
Department of Materials Engineering, Ferdowsi University of Mashhad, Mashhad, Iran. P.O.Box No: ۹۱۷۷۵-۱۱۱۱
A. Kiani-Rashid
Department of Materials Engineering, Ferdowsi University of Mashhad, Mashhad, Iran. P.O.Box No: ۹۱۷۷۵-۱۱۱۱
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :