Carbide Precipitation in the Microstructures of Austempered Ductile Irons Containing ۰.۴۸% and ۴.۸۸% Al
Publish Year: 1384
نوع سند: مقاله ژورنالی
زبان: English
View: 53
This Paper With 8 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ISSIRAN-2-2_001
تاریخ نمایه سازی: 6 آبان 1402
Abstract:
The influence of aluminium on the microstructure of austempered ductile cast iron (ADI) has been studied. The presence of well distributed graphite in the matrix, and a relatively high volume fraction of retained austenite are responsible for the good mechanical properties of the Aluminium alloyed austempered ductile irons including excellent wear resistance, higher resistance to thermal shock, better graphitising tendency and higher resistance to oxidation at high temperatures. A number of specimens of different composition have been made by green sand-casting and gravity die-casting. The transformation to a bainitic microstructure during austempering under different conditions was then examined for the most successful experimental casts. Austenitising temperature of ۹۲۰°C, and austempering temperatures of ۳۵۰°C at different holding times have been used. Microstructures have been examined by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Furthermore, it was found that isothermal transformation at ۳۵۰°C for different soaking times gave a typical bainitic microstructure. Extension of isothermal transformation time leads to precipitation of carbides which also depends on the Al concentration.
Keywords:
Authors
A. Kiani-Rashid
Department of Materials Engineering, University of Sistan & Baluchestan, Zahedan, Iran
D. Edmonds
Department of Materials, University of Leeds, Leeds, UK
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :