Color metallography; a suitable method for characterization of martensite and bainite in multiphase steels
Publish Year: 1388
نوع سند: مقاله ژورنالی
زبان: English
View: 36
This Paper With 5 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ISSIRAN-6-1_003
تاریخ نمایه سازی: 6 آبان 1402
Abstract:
Color metallography is a useful method for characterizing microstructures of steels with multiple phases. In this paper, application of three different color etching techniques for a bainitic-martensitic steel is reported. Comparisons between the results showed that ۱۰% Na۲S۲O۵ aqueous solution was the best etchant for distinguishing martensite, bainite and ferrite phases. The obtained micrographs were clear and sharp. Nanoindentation test was also carried out in order to approve the results of color metallography.
Keywords:
Authors
H. Zakerinia
Department of Materials Engineering, Isfahan University of Technology, Isfahan ۸۴۱۵۶-۸۳۱۱۱, Iran
A. Kermanpur
Department of Materials Engineering, Isfahan University of Technology, Isfahan ۸۴۱۵۶-۸۳۱۱۱, Iran
A. Najafizadeh
Department of Materials Engineering, Isfahan University of Technology, Isfahan ۸۴۱۵۶-۸۳۱۱۱, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :