The Effect of Surface Treatment on Corrosion behavior of Surgical ۳۱۶L Stainless Steel Implant
Publish Year: 1386
نوع سند: مقاله ژورنالی
زبان: English
View: 65
This Paper With 5 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ISSIRAN-4-1_006
تاریخ نمایه سازی: 6 آبان 1402
Abstract:
The AISI ۳۱۶ L Stainless Steel (SS) specimens were exposed to passivation surface through two different processes including; holding in ۴۰-vol% HNO۳ at temperature of ۶۰ ºC for ۳۰ min and ۱۵-vol%H۲SO۴ at ambient temperature for ۱ hour. The corrosion behavior of specimens was evaluated in physiological solutions by electrochemical in vitro tests through linear and Tafel polarization tests. Cyclic polarization tests were performed for investigating of the specimen’s resistance against pitting. Finally, the corrosion resistance of untreated and modified specimens was compared. The results show that the corrosion resistance of ۳۱۶L SS metallic implant is increased due to passivation surface treatment.
Keywords:
Authors
A. Parsapour
Department of Materials Engineering, Isfahan University of Technology, Isfahan ۸۴۱۵۶-۸۳۱۱۱, Iran
M. Fathi
Department of Materials Engineering, Isfahan University of Technology, Isfahan ۸۴۱۵۶-۸۳۱۱۱, Iran
M. Salehi
Department of Materials Engineering, Isfahan University of Technology, Isfahan ۸۴۱۵۶-۸۳۱۱۱, Iran
A. Saatchi
Department of Materials Engineering, Isfahan University of Technology, Isfahan ۸۴۱۵۶-۸۳۱۱۱, Iran
M. Mehdikhani
Department of Materials Engineering, Isfahan University of Technology, Isfahan ۸۴۱۵۶-۸۳۱۱۱, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :