Dynamic Recrystallization by Necklace Mechanism During Hot Deformation of ۳۱۶ Stainless Steel
Publish Year: 1386
نوع سند: مقاله ژورنالی
زبان: English
View: 43
This Paper With 8 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ISSIRAN-4-1_003
تاریخ نمایه سازی: 6 آبان 1402
Abstract:
The aim of this study is to investigate the nucleation of new grains by necklacing mechanism during dynamic recrystallization (DRX). The material used is ۳۱۶ stainless steel. In order to modeling the deformation behavior during hot rolling, one-hit compression tests were performed at temperature range of ۹۵۰-۱۱۰۰ °C with strain rates of ۰.۰۱-۱s-۱. The result shows that at the temperature of ۱۰۰۰ °C with the strain rate of ۰.۱ s-۱, DRX developed by necklace mechanism, it is far from completeness over the steady state stress. By contrast the hardness increased by development of DRX. The final microstructure is very heterogeneous and comprises of very fine and coarse grains due to the occurrence of partial DRX. The results also show that the necklace structure developed by increasing Zener-Hollomon parameter (Z).
Keywords:
Authors
M. Jafari
Department of Materials Engineering, Isfahan University of Technology,.Isfahan, ۸۴۱۵۶-۸۳۱۱۱, Iran
A. Najafizadeh
Department of Materials Engineering, Isfahan University of Technology,.Isfahan, ۸۴۱۵۶-۸۳۱۱۱, Iran
J. Rasti
Department of Materials Engineering, Isfahan University of Technology,.Isfahan, ۸۴۱۵۶-۸۳۱۱۱, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :