Investigation the Anti-Corrosion and Adhesion Properties of Novel MultiCationic Conversion Coating Applied on Steel Substrate
Publish Year: 1397
نوع سند: مقاله ژورنالی
زبان: English
View: 54
This Paper With 16 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ICAC-8-30_005
تاریخ نمایه سازی: 5 آذر 1402
Abstract:
Conversion Coatings are one of the effective ways for improving adhesion of organic coatings to metallic substrates and consequently increasing anti-corrosion performance of a fully coated system. In the current research, multi-cationic conversion coating formed from sources such as hexafluorotitanic acid, sodium molybdate, phytic acid and nickel sulphate was studied and investigated. Results obtained from electrochemical impedance spectroscopy and polarization revealed that conversion coating which formed in the presence of sodium molybdate has not appropriate polarization resistance and the reason for this weak performance investigated by field emission scanning electron microscope. Obtained results showed that in the presence of sodium molybdate, there were abundant micro-cracks on the surface of the coating. After optimizing the multicationic conversion coating, an epoxy coating applied on the surface of bare steel and conversion coated one. The results obtained from adhesion and salt-spray tests indicated that the multi-cationic conversion coating causes improvement in adhesion strength of epoxy coating to steel substrate and finally increased the anti-corrosion performance of the system
Keywords:
Conversion coating , Adhesion , Corrosion , Impedance , Polarization , FE-SEM , پوشش تبدیلی , چسبندگی , خوردگی , امپدانس , پلاریزاسیون , FE-SEM