Effect of Annealing on Physical Properties of Cu۲ZnSnS۴ (CZTS) Thin Films for Solar Cell Applications
Publish place: Journal of Optoelectronical Nanostructures، Vol: 3، Issue: 2
Publish Year: 1397
نوع سند: مقاله ژورنالی
زبان: English
View: 37
This Paper With 10 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JOPN-3-2_002
تاریخ نمایه سازی: 25 بهمن 1402
Abstract:
Cu۲ZnSnS۴ (CZTS) thin films were prepared by directly sputteringCu (In,Ga)Se۲ quaternary target consisting of (Cu: ۲۵%, Zn: ۱۲.۵%, Sn; ۱۲.۵%and S: ۵۰%). The composition and structure of CZTS layers have beeninvestigated after annealing at ۲۰۰ ۰C, ۳۵۰ ۰C and ۵۰۰ ۰C under vacuum. Theresults show that recrystallization of the CZTS thin film occurs and increasingthe grain size with a preferred orientation in the (۱۱۲) direction was obtained. TheRaman spectra showed the existence of crystalline CZTS phase after annealing.Optical transmission spectra were recorded within the range ۳۰۰-۹۰۰ nm. Theenergy band gap (Eg) of the CZTS thin films was calculated before and afterannealing from the transmittance spectra using Beer-Lambert’s law. Results showthat Eg is dependent on the annealing temperature. The optical band gap of CZTSalso varied from ۱.۵۷ eV to ۱.۳۱ eV with increase in the annealing temperaturefrom ۲۰۰ ۰C min to ۵۰۰ ۰C.
Keywords:
Authors
Heydar Izadneshan
Department of physics, Marvdasht Branch, Islamic Azad University, Marvdasht, Iran.
Ghahraman Solookinejad
Department of physics, Marvdasht Branch, Islamic Azad University, Marvdasht, Iran.
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :