ZrO۲ Nanoparticles: Optical Properties of Tetragonal Phase and Enhanced Photocatalytic Activity
Publish place: Journal of Optoelectronical Nanostructures، Vol: 5، Issue: 2
Publish Year: 1399
نوع سند: مقاله ژورنالی
زبان: English
View: 48
This Paper With 12 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JOPN-5-2_002
تاریخ نمایه سازی: 25 بهمن 1402
Abstract:
Tetragonal zirconia (t-ZrO۲) nanoparticles were synthesized from thezirconium chloride using the co-precipitation technique and characterized by variousmeasurement techniques. FESEM analysis further revealed spherical shaped NPs andHR-TEM analysis determined the size of the particles in the range of ۱۴.۵ nm. The bandgap energy was estimated ۴.۰ eV. The UV (۳۵۰ nm) emission was observed from PLspectrum. The photocatalytic degradation of the as-prepared ZrO۲ nanoparticles werestudied under UV light irradiation using ciprofloxacin (CIP) as a model organicpollutant. Results showed that ۵۰% degradation were achieved within ۱۵ min.
Keywords:
Authors
azar bagheri
۱Department of Chemistry, Central Tehran Branch, Islamic Azad University, Tehran, Iran
hana amini
Chemistry, Central Tehran Branch, Islamic Azad University, Tehran, Iran
saeed raayati
۲Department of Chemistry, K. N. Toosi University of Technology, Tehran P. O. Box ۱۶۳۱۵-۱۶۱۸, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :