Enhanced Solar Cell Efficiency with Tin-Based Lead-Free Material (FASnI۳) through SCAPS-۱D Modeling
Publish place: Eurasian Journal of Science and Technology، Vol: 4، Issue: 3
Publish Year: 1403
نوع سند: مقاله ژورنالی
زبان: English
View: 19
This Paper With 9 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_EJST-4-3_008
تاریخ نمایه سازی: 18 اردیبهشت 1403
Abstract:
Recent successes in the development of lead (Pb) halide perovskites have urged extensive research into cost-effective photovoltaic devices, to avoid significant challenges related to stability and toxicity. In this study, device modeling was presented for lead (Pb)-free perovskite solar cells (PSC), by employing FAsnI۳ as the perovskite absorber layer. The simulation evaluates the impact of varying thickness, acceptor density of the hole transport layer (HTL), and temperature within the ranges from ۵۰ to ۲۵۰ nm, ۱x۱۰۱۸ cm-۳ to ۱x۱۰۲۲ cm-۳, and ۳۰۰ K to ۴۵۰ K, respectively. The photovoltaic cell has inverted geometry (p-i-n) and device structure is ITO/PEDOT:PSS/FASnI۳/BCP/Au. The FASnI۳-based PSC exhibits an efficiency of ۱۴.۰۳%, current density (Jsc) ۲۰.۴ mA/cm۲, fill factor (FF) ۷۶.۷%, and open circuit voltage (Voc) ۰.۹۲ V and these results are already presented experimental with same device structure. These results showed that a more eco-friendly solar cell using methyl ammonium tin was created successfully as perovskite. It is suggested to use alternative materials instead of methyl ammonium tin as perovskite.
Keywords:
Authors
- -
Institute of Physics, Baghdad ul Jadeed Campus, The Islamia University of Bahawalpur, Bahawalpur ۶۳۱۰۰, Pakistan
- -
Institute of Physics, Baghdad ul Jadeed Campus, The Islamia University of Bahawalpur, Bahawalpur ۶۳۱۰۰, Pakistan
- -
Department of Physics, University of Education Lahore, DG Khan Campus ۳۲۲۰۰, Pakistan
- -
Institute of Physics, Baghdad ul Jadeed Campus, The Islamia University of Bahawalpur, Bahawalpur ۶۳۱۰۰, Pakistan
Imosobomeh Ikhioya
Department of Physics and Astronomy, University of Nigeria Nsukka, ۴۱۰۰۰۱, Nigeria
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :