Microstructural Evaluation of Pressure Welded Al-1050/AISI-1006steel
Publish Year: 1392
نوع سند: مقاله کنفرانسی
زبان: English
View: 1,215
This Paper With 5 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IMES07_349
تاریخ نمایه سازی: 28 آذر 1392
Abstract:
Joining of dissimilar Al-1050 alloy/AISI-1006 steel was carried out using pressure welding (PW) technique. The microstructures and hardness of the specimen have been investigated. Optical microscope (OM) and Scanning electronmicroscope (SEM) was used to characterize the microstructures of welded zone, heat affected zone (HAZ) and basematerials of bonded samples. The results show that PW can be used the joining of dissimilar Al-1050 alloy and plaincarbon steel. The relationship between the thickness of the welded zone and time of Post Weld Heat Treatment (PWHT) process were studied experimentally. The results show that the thickness of the intermetallic compound increases from 4.5±0.5μm to 5.6±0.7μm as the PWHT time increases from 6 to 24 hr.
Keywords:
Authors
Hengameh Hajipour
Department of Materials Engineering, Yazd University, Yazd, P.O. Box: ۸۹۱۹۵-۷۴۱, Iran
Fariba Nourbakhsh
Department of Materials Engineering, Yazd University, Yazd, P.O. Box: ۸۹۱۹۵-۷۴۱, Iran
Masoud Mosallaeepour
Department of Materials Engineering, Yazd University, Yazd, P.O. Box: ۸۹۱۹۵-۷۴۱, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :