Sol-Gel Synthesis and characterization of nano iron oxide
Publish place: 07th International Congress on Chemical Engineering
Publish Year: 1390
نوع سند: مقاله کنفرانسی
زبان: English
View: 526
This Paper With 9 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICHEC07_504
تاریخ نمایه سازی: 25 فروردین 1394
Abstract:
We have utilized sol-gel method for producing nano structure of xerogel iron oxide with Ferric nitrate nonahydrate as precursor, ethanol as solvent and propylene oxide as gelation agent. Nano oxide at 70°C are produced and evaluated with SEM, TG/DTA, FTIR, and XRD.The results of these analysis confirm the existence of amorph iron oxide, water, γ-Fe2O3, α-Fe2O3, α-FeO(OH) and Fe(OH)3 in this mixture. The morphology of these particles shows that they are spherical andagglomerate because of high reactivity and high surface area.
Keywords:
Authors
Mitra Shirani
Department of Chemical Engineering, Isfahan University of Technology, Isfahan ۸۴۱۵۶-۸۳۱۱۱, Iran
Mohammad Ghoreishi
Department of Chemical Engineering, Isfahan University of Technology, Isfahan ۸۴۱۵۶-۸۳۱۱۱, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :